Impact of low-fusion gutta-percha cones used in variations of the continuous wave condensation technique with filling sealers based on bioceramic compounds on the quality of root canal filling.

To evaluate the impact on the quality of filling with of low-fusion and conventional gutta-percha cones. Thirty-six maxillary canines were prepared and divided into three groups: I-conventional cone with Downpack at 200 °C at 4 mm from the WL; II-low-fusion cone with Downpack at 100 °C up to 4 mm from the WL; III-low-fusion cone with Downpack at 100 °C up to 7 mm from the WL. Temperature variations were measured in thirds on the external surface of the root. The bond strength was evaluated using the push-out test. The adhesive interface was analyzed by scanning electron microscopy. The bond strength and the temperature variation data were analyzed using analysis of variance and the failure type using the chi-square test. The low-fusion cone group with 7 mm Downpack showed higher bond strength (4.2 ± 2.7) compared with conventional cones (2.8 ± 1.6) and low-fusion cones with 4 mm Downpack (2.9 ± 1.6) (p < 0.05), with occurrence of a higher number of adhesive failures to the filling material and mixed failures. Relative to temperature variation, there was less temperature change in the apical third, in the low-fusion cone with Downpack 7 mm (1.0 ± 1.0) (p < 0.05). The use of low-fusion cones allowed the continuous wave condensation technique to be performed at a lower depth of Downpack at 100 °C at 7 mm, with less heating in the apical third, without compromising the quality of filling. Using gutta-percha cones with low fusion, which permits a lower condensation temperature and reduced Downpack depth, maintains the quality of filling, in order to minimize possible damage to the periapical tissues.

Physicochemical properties of calcium silicate cement based endodontic sealers.

AIM: To mensure the physicochemical properties of three ceramic cement endodontic sealers AH Plus Bioceramic, Bio-C Sealer and Bio-C Sealer Ion+ with an epoxy resin sealer, AH Plus. MATERIAL AND METHODS: These properties were measured: hardening time (HT), dimensional change (DC), solubility (SL), flow (FL) and radiopacity (RD). The distilled water obtained from the SL test was analyzed with atomic absorption spectrometry. A sample calculation was made considering n = 5 repetitions for each experimental sealer evaluated. Statistical analysis was performed using one-way ANOVA and post hoc Tukey tests (p < 0.05). RESULTS: For the HT, AH Plus (484 ± 2.76 min) and AH Plus Bioceramic (424 ± 1.23 min) set more slowly than of Bio-C Sealer (370 ± 4.50 min) and Bio-C Sealer Ion+ (380 ± 1.42 min) (p < 0.05). AH Plus Bioceramic (12.56 ± 2.71 %) was more soluble than Bio-C Sealer (6.69 ± 1.67 %), Bio-C Sealer Ion+ (5.67 ± 2.16 %) and AH Plus (0.15 ± 0.01 %) (p < 0.05). AH Plus (0.03 ± 0.01 %) had slight expansion while the cement-based sealers had shrinkage: AH Plus Bioceramic (-1.60 ± 0.63 %) and Bio-C Sealer (-1.38 ± 0.69 %), Bio-C Sealer Ion+ (-5.19 ± 1.23 %) (p < 0.05). Bio-C Sealer Ion+ (59.80 ± 0.86 mm) and Bio-C Sealer (58.60 ± 0.98 mm) had the highest flow compared with AH Plus (56.90 ± 0.56 mm) and AH Plus Bioceramic (49.50 ± 0.63 mm) (p < 0.05). AH Plus (9.17 ± 0.06 mmAl) and AH Plus Bioceramic (8.27 ± 0.84 mmAl) showed radiopacity values when compared with those of Bio-C Sealer (4.90 ± 0.08 mmAl) and Bio-C Sealer Ion+ (4.14 ± 0.05 mmAl) (p > 0.05). CONCLUSION: Ion release is inhered to these cement-based sealers and this result in calcium ion release.

Impact of access cavities on root canal preparation, restorative protocol quality, and fracture resistance of teeth.

The survival of endodontically treated teeth depends on the remaining tooth structure. The aim of this study was to evaluate the impact of different access cavities on root canal preparation, restorative protocol, and fracture resistance of endodontically treated teeth. Fifty-six mandibular molars were divided into control (n=8) and experimental (n=16) groups according to access cavity: Traditional, Conservative, and Truss; and redistributed (n=8) according to instrumentation protocols: Reciproc Blue and R-motion. After, teeth were scanned in micro-CT and then filled and redistributed according to composite resin restoration (n=8): Filtek One BulkFill and Filtek Z350. A new micro-CT scan was performed to analyze the restorative material. Then, samples were submitted to fracture resistance testing and the failure pattern was determined. Data were analyzed using paired T-test, ANOVA, Tukey, and chi-square tests (α=0.05). In Truss, R-Motion promoted less transportation in different thirds of root canals. Higher percentages of voids (5.05%) and filling material (11.7%) were observed in Truss. Fracture resistance values were higher for the control group, followed by Truss, Conservative, and Traditional. The predominant failure pattern was type-II. In Truss, reciprocating instruments with smaller taper showed less canal transportation. Also, Truss provided higher values of fracture resistance, although it presented a higher percentage of voids and remaining filling material. Thus, in Truss, reciprocating files with smaller taper showed less canal transportation, and these cavities provided higher values of fracture resistance, although it presented a higher percentage of voids and remaining filling material.

Influence of bioceramic cones on the quality of root canal filling relative to bond strength and adaptation of the adhesive interface.

AIM: To evaluate the bond strength (BS) and analysis of the adhesive interface in root canals filled with bioceramic gutta percha sealers and cones. MATERIAL AND METHODS: Ninety-six maxillary canines were divided into eight groups according to the endodontic sealer (AH Plus, AH Plus Bioceramic, Bio-C Sealer or Bio-C Sealer Ion+ and gutta percha cones (conventional or bioceramic) tested. They were analyzed using the BS test, failure pattern, analysis of the adhesive interface by scanning electron microscopy and confocal laser scanning microscopy. The BS data were compared between groups using the analysis of variance test with the Turkey post-test. The chi-square test was used to assess the type of failure and the non-parametric Mann-Whitney and Kruse-Wallis tests (P < 0.05). RESULTS: Analysis of variance showed higher BS values for the groups of bioceramic gutta percha cones in Bio-C Sealer Ion+ (8.38 ± 4.27), AH Plus Bioceramic (6.19 ± 3.28), Bio-C Sealer (5.70 ± 3.18), AH Plus (4.61 ± 2.11) and for conventional gutta percha cones in AH Plus sealers (4.26 ± 2.35), Bio-C Sealer Ion + (3.63 ± 2.29), Bio-C Sealer (2.94 ± 2.32) and AH Plus Bioceramic (1.19 ± 0.89) (P < 0.05). Relative to the type of failure and adaptation of the types of filling material, a higher percentage of mixed failures was observed (gaps between 1 µm-10 µm) for the group with bioceramic gutta percha cones (P < 0.001). CONCLUSION: The bond between sealers and bioceramic gutta percha cones showed higher bond strength values and greater penetration into the dentin tubules. CLINICAL RELEVANCE: The filling the root canal system with bioceramic sealers should be associated with bioceramic gutta percha cones.

Chemical, morphological and microhardness analysis of coronary dentin submitted to internal bleaching with hydrogen peroxide and violet LED.

BACKGROUND: Violet LED has been used for internal bleaching, however its implications on coronary dentin composition are unclear. The present study aims to evaluate the effect of bleaching with violet LED, either associated with 35 % hydrogen peroxide or not, on microhardness, chemical composition, and morphological characteristics of coronal dentin. METHODS: Thirty maxillary canines were selected to obtain 30 blocks of coronal dentin, distributed in 3 groups (n = 10): 35 % hydrogen peroxide (HP); violet LED (LED); HP 35 % + LED, (HP+LED). The chemical analysis was performed by FTIR and the morphological evaluation of the dentin structure by confocal laser scanning microscopy before (T0) and after treatment (T1). The microhardness analysis was performed by microdurometer after bleaching. The data were submitted to repeated measures ANOVA test (P> 0.05). RESULTS: The intensity of the inorganic peaks decreased after bleaching for all groups (P = 0.003). There was an increase in the organic peak intensity after bleaching with HP, a decrease for LED, while HP+LED did not change the intensity (P = 0.044). Moreover, the inorganic/organic ratio decreased for HP (P = 0.022), while for LED and HP+LED there was no significant changes (P>0.05). HP and HP+LED showed lower microhardness values compared to LED (P< 0.05). Regarding morphological changes, an increase in the perimeter of the dentinal tubules was found for all groups, with the smallest increase being observed for LED. CONCLUSION: HP bleaching decreased the chemical stability and microhardness of the coronal dentin, while the violet LED treatments had no significant impact on dentin stability. In all groups, there was an increase in exposure of the dentinal tubules after bleaching, which was less pronounced with the violet LED bleaching.

An automated method to analyze root filling voids and gaps using confocal microscopy images.

This study evaluated the feasibility of an automated method to delimit the required area to quantitatively analyze root filling voids and gaps from cross-sectional confocal laser scanning microscopy (CLSM) images. Root canals of maxillary canines were prepared with rotary instruments and filled by lateral compaction technique using gutta-percha and AH Plus sealer. The roots were stored (100% humidity, 37 °C) for a period of 24 h and then transversally sectioned to obtain 2-mm-thick slices from the apical and middle thirds. The areas corresponding to filling materials, gaps, and voids were manually delimited or automatically demarked by ImageJ software after converting the images to the RGB color system. Based on manual and automatic delimitations, the percentages of voids and gaps were calculated. Data of voids and gaps between middle and apical thirds were individually compared by paired t-test. Pearson`s correlation test was used to assess the correlation of data between the methods. Irrespective of the method of area delimitation, no difference was observed between the root thirds for both voids and gaps, while the p-values calculated for each method were similar. Almost perfect correlations between the methods were observed for both outcomes. The proposed method to automatically delimit the areas corresponding to filling material, voids, and gaps appears to be a valid method to facilitate the quantitative analysis of defects in root canal fillings using topographic CSLM images.

Canal Drying Protocols to Use with Calcium Silicate-based Sealer: Effect on Bond Strength and Adhesive Interface.

INTRODUCTION: The aim of this study was to evaluate the influence on bond strength and interface quality of different canal drying protocols in roots filled with Bio-C Sealer (BCS; Angelus, Londrina, Paraná, Brazil). METHODS: Ninety-six roots of upper canines were prepared with an R50 file (Reciproc; VDW GmbH, Munich, Germany) and irrigated with 2.5% sodium hypochlorite and 17% EDTA under ultrasonic agitation. Roots were divided according to the drying protocol as follows: dry, the White Mac tip (Ultradent, Indaiatuba, SP, Brazil) for 5 seconds followed by aspiration with a capillary tip for 5 seconds and paper points; slightly moist, the White Mac tip followed by capillary aspiration without paper points; wet, the White Mac tip followed by a single paper point. The roots were filled with BCS or AH Plus (AHP; Dentsply Maillefer, Ballaigues, Switzerland) (n = 16) and sectioned for the push-out test after 3 months. Failure modes were assessed, and the interface morphology was analyzed under scanning electron microscopy. After 6 months, the other half of the roots were evaluated. Data were analyzed by analysis of variance/Tukey test at 5%. The chi-square test was used in the failure analysis and the Kruskal-Wallis/Dwass-Steel-Critchlow-Fligner for interface analysis. RESULTS: The AHP-filled roots had the highest bond strength when the canal was dried (P < .05). No difference was found for periods (P > .05). For BCS, the highest bond strength was found in the slightly moist canals (P < .05). A predominance of adhesive failures was observed. The dried canals filled with AHP had the highest percentage of good adaptation, whereas BCS had no difference. CONCLUSIONS: The best drying protocol for AHP is using the White Mac tip followed by capillary tip aspiration and paper points until complete dryness, and for BCS, it is using the White Mac tip followed by capillary aspiration without paper points.

Analysis of the adhesive interface of dentine treated with carbodiimide and chitosan before cementation of fiberglass posts with different resin cements.

The objective of this study is to evaluate the effect of 1-ethyl-3-(3-dimethylaminopropyl)-carbodiimide (EDC) and chitosan (CHI) on the adhesive interface of resin cements to root dentine. Forty-five upper canines were sectioned, endodontically treated, prepared and divided into three groups according to dentine treatment (distilled water-DW, CHI 0.2% and EDC 0.5) and in three subgroups according to resin cement: RelyX ARC, Panavia F 2.0 or RelyX U200. Slices were obtained, with five slices of each third submitted to the analysis of the adaptation of the adhesive interface through scores and the perimeter with gaps in confocal laser scanning microscopy and one slice of each third later evaluated qualitatively in scanning electron microscopy. The results were analyzed using with Kruskal-Wallis and Spearman correlation tests. There was no difference in adaptation for the different resin cements (p = .438). EDC presented better adaptation when compared to the groups treated with DW and CHI (p < .001), while the CHI and DW presented similar adaptation values (p = .365). No difference was observed in the perimeter referring to the gap areas for the different resin cements (p = .510). EDC showed a lower percentage of perimeters with gaps when compared to CHI (p < .001), with the percentage of perimeter with gaps of teeth treated with CHI being lower than DW (p < .001). A positive correlation coefficient equal to 0.763 was obtained between the perimeter with gaps and the adaptation data of the adhesive interface (p < .001). EDC resulted in better adaptation of the adhesive interface and a lower percentage of perimeters with gaps compared to chitosan.

Prevalence and morphological analysis of dens invaginatus in anterior teeth using cone beam computed tomography: A systematic review and meta-analysis.

OBJECTIVES: To evaluate the prevalence and morphological characteristics of DI using CBCT. METHODS: A literature search was performed in PubMed, Embase, Scopus, and Web of Science. Inclusion criteria were randomized clinical trials, cross-sectional studies, and prospective and retrospective cohort studies evaluating the morphological characteristics of DI in anterior teeth using CBCT. Three reviewer authors independently screened the studies, applied the eligibility criteria, assessed the risk of bias, and extracted until September (2022). The risk of bias was evaluated using the Joanna Briggs Institute criteria. Meta-analyses of proportions were used for estimate the prevalence DI according to factors at participant and tooth levels. RESULTS: Six studies were included in the meta-analysis. Among 7373 individuals, a prevalence of 7.45 % of DI was observed (n = 258; τ2 = 0.0096; CI of 4.51-11.3; p < 0.05), with no significant influence of sex. Regarding laterality, unilateral DI showed higher mean prevalence (4.30 %; CI of 2.03-7.33). Among the 382 anterior teeth with DI (0.72 %), the most affected tooth was the upper lateral incisor (5.12 %; n = 329; CI of 2.35-8.86; p < 0.001), type I was the most prevalent (0.59 %; CI of 0.24-1.08) and the presence of open apex and periradicular pathology ranged from 4.3 % to 22.72 % and 3.5-77.92 %, respectively. CONCLUSIONS: The prevalence of individuals with dens invaginatus was 7.45 %, the most affect tooth was the upper lateral incisor with a prevalence of 5.12 % unilaterally and type I was the most prevalent morphology.

Effect of Carbodiimide (EDC) on the Bond Strength Longevity of Epoxy Resin-based Endodontic Sealer to Root Dentin: An In-Vitro Study.

PURPOSE: EDC (1-ethyl-3-(3-dimethylaminopropyl)carbodiimide hydrochloride) can increase dentin bonding longevity. This study aimed to evaluate the effect of final irrigation of the root canal with EDC on the bond strength (BS) longevity of an epoxy resin-based root-canal sealer. MATERIALS AND METHODS: Twenty maxillary canines were sectioned and standardized for root length at 17 mm. Roots were instrumented and distributed into 2 groups according to the final irrigation protocol: EDTA 17%+NaOCl 2.5% (C) and EDTA 17%+NaOCl 2.5%+EDC 0.5M (EDC). The canals were dried and filled with AH Plus (Dentsply Sirona). Three slices were obtained per third, and the first slice from each third was used for the immediate push-out test (i) followed by analysis of the failure pattern (n = 10); the second slice from each third was used for the push-out test after 6-month aging (A) followed by analysis of the failure pattern (n = 10); the third slice from each third was used to examine the adhesive interface under confocal laser scanning microscopy (CLSM) (n = 10). Data were analyzed with ANOVA, Fisher's exact and Kruskal-Wallis tests. RESULTS: Higher BSs were found for EDC-A (5.6 ± 1.9) than for EDC-I (3.3 ± 0.7), C-i (2.5 ± 1.0) and C-i (2.6 ± 1.0) (p = 0.0001), while C-A values were in some cases similar to C-i and in others similar to EDC-i. No statistically significant difference was observed between the thirds (p > 0.05), except for EDC-i, which showed lower BS for the cervical (2.79 ± 0.46) compared to the apical third (3.8 ± 0.5), while the middle third in some cases had values similar to those of the apical and in others to the cervical third (3.2 ± 0.7) (p = 0.032). More mixed adhesive failures were found in the cervical third, and more adhesive failures to the sealer occurred in the middle and apical thirds (p = 0.014). A significant difference was observed between treatments in terms of adaptation of the adhesive interface, with a higher percentage of good adaptation using EDC (66.7%) than using C (40%), and a lower percentage of poor adaptation with EDC (10%) compared to C (20%) (p < 0.05). CONCLUSION: Root canal irrigation with EDC increased the longevity of the adhesive interface of an epoxy resin-based root-canal sealer.

Evaluation of the push-out bond strength of an adjustable fiberglass post system to an endodontically treated oval root canal.

To evaluate the push-out bond strength of the adjustable fiberglass post system to dentin. Twenty maxillary canine roots were endodontically treated and divided into two groups (n=10): conventional fiberglass posts (CFPs) and with single adjustable post (SAP) system. Two slices of each third were subjected to the push-out and failure pattern test and the most apical slice was subjected to analysis of the adhesive interface by scanning electron microscopy (SEM). Data were analyzed by the three-way analysis of variance, Tukey, and Friedman tests, and linear regression (α=0.05). The results showed higher push-out bond strength in the initial time interval for SAP (10.3±5.3, p<0.01). After 6 months, there was reduction in push-out bond strength for both (p<0.001). A higher percentage of adhesive and cohesive failures to dentin. After 6 months areas of maladaptation were noted (p=0.000). The SAP is completed to the promissory root canal in relation to alternative CFP.

Impact of access cavities on root canal preparation, restorative protocol quality, and fracture resistance of teeth

Abstract The survival of endodontically treated teeth depends on the remaining tooth structure. The aim of this study was to evaluate the impact of different access cavities on root canal preparation, restorative protocol, and fracture resistance of endodontically treated teeth. Fifty-six mandibular molars were divided into control (n=8) and experimental (n=16) groups according to access cavity: Traditional, Conservative, and Truss; and redistributed (n=8) according to instrumentation protocols: Reciproc Blue and R-motion. After, teeth were scanned in micro-CT and then filled and redistributed according to composite resin restoration (n=8): Filtek One BulkFill and Filtek Z350. A new micro-CT scan was performed to analyze the restorative material. Then, samples were submitted to fracture resistance testing and the failure pattern was determined. Data were analyzed using paired T-test, ANOVA, Tukey, and chi-square tests (α=0.05). In Truss, R-Motion promoted less transportation in different thirds of root canals. Higher percentages of voids (5.05%) and filling material (11.7%) were observed in Truss. Fracture resistance values were higher for the control group, followed by Truss, Conservative, and Traditional. The predominant failure pattern was type-II. In Truss, reciprocating instruments with smaller taper showed less canal transportation. Also, Truss provided higher values of fracture resistance, although it presented a higher percentage of voids and remaining filling material. Thus, in Truss, reciprocating files with smaller taper showed less canal transportation, and these cavities provided higher values of fracture resistance, although it presented a higher percentage of voids and remaining filling material.

The impact of provisional intraradicular retainers cementation with temporary methacrylate-based resin in the bond strength of glass fiber posts to root dentin.

Chemical composition of temporary cements interferes in the bond strength and quality of the bond interface of glass fiber posts to root dentin. The aim of the present study was to evaluate the influence of different temporary cements on the bond strength of fiberglass posts and resin cement. Thirty-two maxillary central incisor roots were standardized at 15 mm length. The root canals were prepared with Reciproc R50 and filled with a R50 single cone and AH Plus. Ten mm of filling material was removed with a heated Schilder condenser, leaving 5 mm of apical filling material. The roots were randomly distributed into 4 groups (n = 8). In the control group, the root canal was prepared with a standard drill according to the post diameter (DC #1, FGM, Joinville, Brazil), irrigated with 5 mL of distilled water and immediately received the fiberglass post cemented with self-adhesive resin cement. For the other groups, cores were made with temporary intraradicular retainers cemented with different temporary cements: methacrylate-based resin (Bifix Temp - Voco), calcium hydroxide-based (Provicol - Voco) and zinc oxide-based - eugenol-free (Relyx Temp NE - 3M). After 7 days, mechanical removal of the temporary retainers, preparation, irrigation of the root canal and cementation of the fiberglass post were performed, following the same protocol that had been performed in the control group. The roots were sectioned to obtain 3 slices per root third. The most cervical section of each third was used for the push-out test and failure pattern analysis, while the most apical section was subjected to analysis of the adhesive interface by scanning electron microscopy (SEM). The BS data were compared between groups using the two-way ANOVA and Tukey post-test. The failure pattern results were expressed in percentage and compared between groups using the chi-square test and the material adaptation data at the bond interface were evaluated using the Kruskal-Wallis and Dwass-Steel-Critchlow-Fligner tests. The results showed higher BS in the cervical third, with a higher value in the control group (10.8 ± 0.94) and Bifix Temp group (9.78 ± 0.71), with no statistically significant difference between these groups (P > .05). The middle and apical thirds showed no statistically significant difference (P > .05). As regards the type of failure, a higher percentage of mixed adhesive failures was observed for all groups. Analysis of the adhesive interface by SEM showed that the temporary cement Bifix Temp showed greater adaptation at the bond interface. It was concluded that the methacrylate-based resin temporary cement showed the highest bond strength values and best adaptation to root dentin than the zinc oxide-based and calcium hydroxide-based temporary cements.

Bleaching effect of violet LED of 405-410 nm on stained endodontically treated teeth.

AIM: To evaluate in vitro the whiteness index (WID) and the whiteness index variation (ΔWID), as well as the color stability of stained endodontically treated teeth after bleaching with violet LED (VL) and with hydrogen peroxide 35% (HP) associated or not to VL. METHODS: Twenty-four lower incisors were selected. The color was measured using a spectrophotometer at the following times: baseline, after staining, bleaching, and thermocycling, to determine the whiteness index and variation (WID and ΔWID). For the staining process, the teeth were immersed in human blood and centrifuged. After biomechanical preparation, the specimens were distributed into three groups (n = 8): control group (HP); violet LED (VL); and HP 35% + VL (HP+VL), and one session was performed for both bleaching procedures every week for three weeks, followed by thermocycling, where 10,000 cycles were performed. After color analysis, the data obtained were submitted to statistical analysis (RM ANOVA, p < 0,05). RESULTS: The staining of the teeth reduced the WID values for all experimental groups compared to baseline, and the bleaching protocols increased WID values, with the lowest WID values for group VL. There was no statistically significant difference after thermocycling for all groups compared to bleaching. Staining and thermocycling reduced the ΔWID values, and no difference was found between treatments at these assessment times. Bleaching increased the ΔWID values, with less pronounced changes in the VL group. CONCLUSION: VL used alone has a lower bleaching effect compared to the bleaching treatment with HP, whether or not associated with VL, and the color stability was observed for all groups.

Is the quality of root canal filling obtained by cone-beam computed tomography associated with periapical lesions? A systematic review and meta-analysis.

AIM: To evaluate the influence of root canal filling quality on periapical lesion status using cone-beam computed tomography (CBCT). MATERIALS AND METHODS: The bibliographic search was conducted in electronic databases of PubMed, Embase, Scopus, and Web of Science without restrictions related to the year of publication and language. Inclusion criteria were prospective or retrospective cohort studies that followed periapical pathosis for, at least, 1 year. Three reviewers independently evaluated the eligibility for inclusion, extracted data, and assessed the risk of bias. The quality of the studies was based on the Newcastle-Ottawa Scale. This meta-analysis was performed to evaluate the quality of treatment by the homogeneity and apical extension of the filling. RESULTS: Of the 1179 studies initially recovered, six cohort studies were included, out of which four were considered with a low risk of bias. The results showed that the absence of gaps in the filling reduced the chance of unhealed periapical lesions by 2.39 times (RR = 2.39; 95% CI: 1.62-3.53; p < 0.00001; I2 = 55%). An apical filling extension of 0-2 mm below the apex also contributed significantly to the absence of unhealed periapical lesions (RR = 1.49; 95% CI: 1.15-1.94; p = 0.003; I2 = 2%). CONCLUSION: The homogeneity and apical extension of the filling influenced the presence of unhealed periapical lesions in endodontically treated teeth evaluated using CBCT. CLINICAL RELEVANCE: Apical extension of the filling ranging between 0 and 2 mm short of the apical foramen and the homogeneity of the filling without gaps are directly related to the success rate of root canal treatment.